A quick-drying, modified alkyd resin based primer with lead-free corrosion inhibitors. It has excellent anti corrosive
property and provides economic advantages by decreasing the number of coatings. And it is widely used in marine and
heavy duty coating industry.
Approved as a Fire Retardant Coating by Lloyd's Register of Shipping (LR), Korean Register of Shipping (KR), Det Norske
Veritas (DNV, CE Marking) and Germanischier Lloyd (GL)
Recommended Recommended
use use
High build anti-corrosive primer for non-immersed steel structures of vessels and other projects which
are subjected to expose to moderate and severe atmosphere such as coastal and marine environments
Physical Properties Physical Properties
Finish and Finish and
Color Color
Flat. L/Grey (1105), Red (2272)
For application where light color topcoats are used or only one topcoat application is specified, use grey
to facilitate better hiding from the topcoat
Specific Specific
gravity gravity
Approx. 1.3
Solids by Solids by
volume volume
Approx. 44 % (Determined by ISO 3233)
Spreading rate Spreading rate
(Theoretical) (Theoretical)
6.28 ㎡/L in 70 ㎛ dry film thickness on a smooth surface.
Flash point Flash point 31 ℃/88 ℉ (Closed cup)
Chemical Chemical
Resistance Resistance
Acids Alkalis Solvents Salts Water
Splash & Spillage NR NR NR Good Excellent
Fumes Poor Poor Poor Good Excellent
Immersion NR NR NR NR NR
* NR : Not Recommended
Application details Application details
Surface Surface
preparation preparation
Remove any oil, grease, dirt and any other contaminants from the surface before painting by proper
method such as solvent cleaning and fresh water washing, etc.
* Steel : Blast cleaning to Sa2.5 or Power tool cleaning to St3, St2, etc
Method of Method of
application application
Spray (Airless or Air), Roller or Brush application.
For airless spray application ;
Nozzle orifice : 533 ㎛ ~ 584 ㎛ (0.021″ ~ 0.023″)
Output pressure : 19.7 MPa
Fan : 60 °
(Airless spray data are indicative and subject to adjustment)
Thinning Thinning Thinner No. 002
Application Application
conditions conditions
The surface should be completely cleaned and dried. Do not apply when relative humidity is above 85%.
The surface temperature should be at least 2.7℃(5℉) above dew point to prevent condensation. In
confined, areas, ventilate with clean air during application and drying to assist solvent evaporation.
Film thickness Film thickness 70 ㎛ dry.
Depending on the purpose and the area of use, different film thickness may be applied
Drying time Drying time Substrate temperature 5 ℃/41 ℉ 20 ℃/68 ℉ 30 ℃/86 ℉
Set to touch 6h 2h 1h
Dry through 12h 4h 3h
* The actual drying time is subject to the film thickness, ventilation, humidity etc.,
and drying time under other temperature conditions should be checked and informed by KCC
Subsequent Subsequent
Coat Coat
Koramel Enamel LT313 or according to specification.
Recoating Recoating
interval interval
At 20 ℃/68 ℉, Minimum : 8 h
Maximum : Free
Before overcoating, remove the oil, salt, chalking material and any other contaminants on aged coating
film completely by proper cleaning method such as solvent cleaning and/or fresh water washing.
Heat Heat
resistance resistance
temperature temperature
Continuous : 93 ℃/200 ℉(Non-immersion service)
Non-continuous : 121 ℃/250 ℉(Non-immersion service)
Storage and package Storage and package
Shelf life Shelf life 36 months
Packing Unit Packing Unit 4l, 18 L
Remarks Remarks
Handling Handling
Precautions Precautions
Protect skin and eyes from direct contact with liquid paint, and avoid prolonged breathing of solvent
vapors.
Respiratory protection is recommended during application in confined spaces or stagnant air.
1'st issue 1'st issue 2012-03-01
Revision Revision 2019-07-26